Process control

Juncheng pipeline JCCO —— build “China TQC more strict pipeline”, product through 219 inspection link control product quality.

Control test items	Control detection effect	working procedure	Control and detection link	Control test content
Selected manufacturers	Ensure raw material manufacturer qualification and product quality	1	Evaluation of raw material manufacturers	Quality, credibility and other aspects of comprehensive evaluation, raw material procurement to achieve“quality selection of raw materials”
Selected manufacturers		2	Verify information	Check the information of raw materials provided by the supplier, and enter the yard only after they are correct
Selected raw materials	Raw materials for welded pipe production directly affect the quality of welded pipe	3	Scab examination	Avoid "on the surface of the roll plate; Tongue shape &; Or & lt; Scale &; Of, bonded, irregularly shaped raised metal sheet
		4	Crack inspection	Avoid the gap between the top and bottom of the coiled plate
		5	Layered inspection	Avoid local and obvious metal separation layer on coil section
		6	Bubble inspection	Avoid irregular and round holes with smooth inner wall on the surface or inside of the coil board
		7	Surface slag inclusion inspection	Avoid non-metallic slag inclusion on the surface of rolling plate
		8	Pitting inspection	Avoid small and irregular pits and local rough surface on the surface of rolling plate
		9	Scratch inspection	Avoid straight and fine groove mark on the surface of coil plate
		10	Scratch inspection	Avoid slight straight or curved scratches on the surface of the coil
		11	Indentation inspection	Avoid different shape, size and intermittent dents on the surface of the rolling plate
		12	Roller printing inspection	Avoid the damage of the pressure roller and make the surface of the coil periodically appear convex or concave marks
		13	Rust inspection	Avoid yellow, yellow green, or brown spots on the local surface of the coil
		14	Scale inspection	Avoid too large area of red metal oxide layer formed on the surface of coil plate
		15	Piao Qu inspection	Avoid bending in both longitudinal and transverse directions
		16	Sickle bend inspection	Accord with GB/T 3524—2005 standard（P2）requirement
		17	波浪检查	避免在卷板的全长或局部沿轧制方向的水平面呈起伏不平的且有规律分布的突出（波峰）和凹下（波谷）的弯曲形状
		18	浪皱检查	避免沿轧制方向在卷板的一侧出现起伏不平的海带状弯曲
		19	槽状检查	避免卷板沿横向两侧边同时发生的弧形弯
		20	厚度不均检查	避免卷板纵、横断面厚度不均
		21	毛刺检查	避免在卷板宽度方向的两边出现尖而薄的飞刺
		22	折叠检查	避免使卷板发生的急剧弯曲而形成的折痕或搭迭
		23	宽度检测	防止宽度及其均匀性不符合 GB/T 3524—2005 标准（P4）或采购要求
		24	厚度检测	防止厚度及其均匀性不符合 GB/T 3524—2005 标准（P3）或采购要求，做到“壁厚确保标准”
		25	成分分析	按照 GB/T 4336 标准分析 C、Si、Mn、P、S，结果与来料材质单进行比较，避免材质不符合 GB/T 700 标准要求（P4）
		26	力学试验	按照 GB/T 228 标准对卷板进行横向或纵向拉伸试验，结果与来料材质单进行比较，避免力学性能达不到 GB/T 3524—2005 标准要求（P5）
卷板裁剪	将卷板裁剪成生产不同规格焊管的卷板	27	进料检查	避免卷板表面及边缘有磕碰损坏
		28	剪切检查	检查液压剪子，剪切不齐，切头不得超过有效板面2cm（. 卷板尾部应到机组进行处理
		29	导向辊检查	调整导向辊，防止漏刀
		30	接头检查	避免接头处不平整、焊缝余高不符合 GB/T3091—2015 标准（P8）
		31	圆盘剪检查	检查刀轴和刀套，防止刻刀和原料裁剪的宽窄不均
		32	卷曲检查	进料不能太长，防止卷曲脱落
		33	分料盘检查	防止卷板有漏刀、毛刺、扣边现象
上料转盘	放入卷板，保证卷板打入料笼前准备	34	外观检查	防止卷板表面及边缘有磕碰损坏
卷板切头	将卷板料窄处剪掉，便于焊接	35	剪切要求	将卷板料窄处剪切整齐，与卷板方向垂直，且带头长度部分不得超过有效板面 2cm
卷板对焊	将不同卷的卷板连接在一起送入料笼	36	外观检查	避免接头处不平整、焊缝余高不符合 GB/T3091—2015 标准（P8）
打入料笼	为机组储存一定量的原料，保障机组连续开车生产	37	外观检查	防止表面及边缘有磕碰损坏现象
打入料笼	为机组储存一定量的原料，保障机组连续开车生产	38	打料检查	防止卷板在笼套内卡死或翻料
五辊平整	原料与轧辊同一中心	39	五辊平整	由于卷板在料笼储存时会出现折弯，通过五辊方可较平
钢管成型	将卷板由粗成型转变成精成型（卷成圆管型）	40	成型质量检查	保证焊缝开口角的平整与对称，可根据管径对开口角进行调整。（4 分—1.2 寸开口角为 3—5 度）
挤压成型	保证管坯两边水平性	41	挤压辊检查	防止高低不平，观察挤压辊的挤压力，保持同一高度
高频焊接	将卷成圆筒型的卷板焊接牢固	42	焊接质量检查	避免焊接不牢，脱焊，冷叠
		43		避免焊缝两边出现波纹
		44		避免焊缝有开裂与静裂
		45		避免焊缝不能形成线状
高频焊接	将卷成圆筒型的卷板焊接牢固	46	焊接质量检查	避免出现夹渣
		47		避免出现焊缝外裂纹
		48		避免出现根部收缩
		49		避免出现根部未焊透
		50		避免出现未熔合
		51		避免出现漏焊、假焊、搭焊等现象的出现。（一般卷板在通过加紧辊时，由于高频加热卷板边缘熔化，在焊接时会出现乳白色的晶体颗粒状火花，这说明焊接质量是有保证的）
焊缝刮疤	对外焊缝余高进行削磨处理	52	外观检查	防止转缝、免口及焊口错位现象；要求焊缝无波纹，两侧无焊瘤。
焊缝刮疤	对外焊缝余高进行削磨处理	53	焊缝检查	保证焊缝刮痕、颜色和成型质量情况符合 GB/T13793—2008（P10）要求
循环冷却	对焊管进行冷却	54	水槽水容量检查	根据管径不同，速度快慢，控制水质、水温、水流量、含盐量、酸碱度等
钢管定径	调整焊管外径及不圆度	55	外径检查	控制在 GB/T21835—2008 标准（P5）要求范围内
钢管定径	调整焊管外径及不圆度	56	不圆度检查	控制在 GB/T3091—2015 标准（P4）要求范围内
粗略调直	消除钢管轻微弯曲	57	观察调直设备	使用调直设备，使钢管平直进入下一道工序
无损检测	检测焊缝表面及内部可能影响钢管质量的缺陷	58	检测前仪器调校	设置相关参数；用对比试块确定扫查比例及探伤灵敏度；增加表面补偿，以保证缺陷的检出率
		59	更换规格后首批检验	每次更换产品规格开车后必须进行首批成品检验，检验支数不少于三支，合格后方可生产
		60	焊管基体金属检验	通过目视检查钢管表面的质量缺欠
		61	焊缝外观检验	通过目视检查冷却后的焊缝外观，不允许有焊缝错位、烧伤、结疤、开口、裂缝、筋裂刮疤不平、免口等缺陷存在
		62	金属及焊缝内部质量超声波检测（抽检）	紧贴管体的探头发射超声波，仪器接受并解析反射的回波，根据 SY/T6423.2—1999 调校探测基准灵敏度，通过仪器屏幕上显示的回波波高判断反射体的类型、大小、深度。不允许存在裂纹、回波波高超过满屏 50% 的气孔、未焊透、未融合等严重影响焊缝质量的缺陷。抽检规则：按照每批次 1% 比例进行抽检，如发现问题及时记录和反馈。在缺陷处做好明显的标记，便于工人进行相应的处理；并增加 10% 的抽检率增加抽检过程中仍然存在不合格品，应及时通知机组停车调整生产工艺
飞锯切割	对焊管定尺切割	63	管端检查	管端保证无毛刺、斜口
飞锯切割	对焊管定尺切割	64	定尺长度	根据标准检查测速辊直径，设定合理数据
钢管矫直	调整钢管弯曲度	65	外观检查	避免管体损伤、管口压扁现象；管面不能有压痕
管端齐头	将管口毛刺处理干净	66	管端检查	保证管端光滑无毛刺，保证每根钢管达到“管直头净效果”
成品检验	保证出车间焊管质量符合标准要求	67	外观检查	保证表面钢管表面光滑，不允许有折叠、裂缝、重皮、分层、搭焊等缺陷存在，允许有壁厚负偏差范围的划伤，不允许有严重划伤、焊缝错位、烧伤和结疤
		68	内焊缝检查	保证焊筋牢固，粗细均匀，呈铁丝状，内焊筋应高于 0.5mm，穿线管焊筋不允许有毛刺存在
		69	外径检查	控制在 GB/T21835—2008 标准（P5）要求范围内
		70	不圆度检查	控制在 GB/T3091—2015 标准（P4）要求范围内
		71	定尺长度检测	钢管长度为 6m，根据 GB/T3091—2015 要求直缝高频焊管的总长度允许偏差为 +20mm。（君诚专用管要求：4 分—2 寸 0—5mm、2.5 寸—4 寸 0—10mm、5 寸— 8 寸 0—15mm）
		72	弯曲度检测	根据 GB/T3091—2015 要求钢管全长弯曲度应不大于钢管长度的 0.2%
		73	管端检测	保证管头无毛刺，端头截面符合 GB/T3091—2015 要求
		74	外焊缝检查	外焊缝刮疤应使用圆弧刀，刮疤处应圆弧过渡
		75	豁口检查	避免在管端有开豁现象
		76	裂缝检查	避免在焊筋处有开裂现象
		77	接头检查	避免焊管管体上有对接现象
		78	划伤检查	避免焊管表面有严重划痕，影响壁厚。不能低于壁厚的负偏差（12.5%）
		79	瘪坑检测	防止在焊管局部因外力造成坑凹现象。企业内控标准（4 分—1 寸，瘪坑深度 <2mm；1¼ 寸—2 寸，瘪坑深度 <3mm；2½ 寸—6 寸，瘪坑深度 <4mm；8 寸瘪坑深度 <6mm）
		80	麻面（坑）检查	避免钢管表面有点状的凹痕
		81	内焊筋检查	防止焊筋不牢固、不均匀，低于 0.5mm 为焊筋不合格
		82	毛刺检查	避免管头内外面有不规则的多余部分。企业内控标准（4 分—2 寸毛刺<1mm；2½ 寸— 4 寸毛刺 <2mm；5 寸—8 寸毛刺 <3mm。注：净头管不允许有毛刺）
		83	吊口检查	避免由于挂钩、吊装造成的豁口或变形即“吊口”
		84	筋裂检查	防止在焊筋部位产生细小裂纹
成品检验	保证出车间焊管质量符合标准要求	85	刮疤不平	避免刮疤后焊筋上凹凸不平，焊筋处不是平滑的圆弧面，低于母材的负差视为不平
		86	免口检查	防止由原料或机械原因造成的焊缝处折叠、重压现象，焊筋部位不光滑，有免边、折叠焊缝错位等
		87	重皮检查	避免表面不光滑、有分层、少肉或高低不平现象
		88	结疤检查	避免表面有对母材构成伤害的焊点
		89	砂眼检查	防止钢管表面有孔
		90	斜口检查	防止管的横截面与中心线不垂直，端头应符合 GB/T3091—2015 要求
		91	标识检查	避免管体所粘商标与焊管的实际规格不符或混批
成品包装	依照每件规定数量的钢管进行打包	92	打包带检查	钢管包装为六角形，6 道打包带，均为本厂生产，两端打包带距端 130mm±10mm，中间 4 道要均分，打包带焊接时应对齐、平整，打包带不允许偏斜，打包带对接处应切 45°角，必须符合 GB/T2102—2006（P5）要求
成品包装	依照每件规定数量的钢管进行打包	93	商标检查	内容准确，平面朝上，成品管商标要端正贴在每件管挡板对齐第一道焊接打包带右侧面中间，君诚字迹向内
力学试验	检验材料力学性能	94	弯曲试验	检验 2 寸及以下钢管焊接质量，符合 GB/T3091—2015（P7）要求
		95	压扁试验	检验 2 寸以上钢管焊接质量，符合 GB/T3091—2015（P7）要求
		96	压槽试验	检验钢管压槽性能，符合CECS 151-2003 沟槽式连接管道工程技术规程要求（P9）
		97	拉伸试验	检验钢管抗拉强度及断后伸长率，符合 GB/T3091—2015（P7）要求
水压检验	检查焊管基体金属和焊缝的强度、密闭性及外观质量	98	拆包前检验	避免标签与焊管的实际规格不符或混批不允许拆包（同一炉批号、同一规格一起打压
		99	外观检验	目视检查基体金属 , 防止有裂缝、重皮、严重锈蚀、砂眼等缺陷 , 不允许严重划伤
		100	试验开始前端头检验	通过目视检查焊管两端头表面必须平整光滑。不允许有瘪头、弯管、吊口，端口无毛刺管端头截面与中心线垂直，无斜面，偏差应小于 3°
		101	增压前充填传压介质（水）检验	焊管充填传压介质（水）完毕后，不要急于升压，必须先检查一下系统有无渗液漏液现象
		102	静水压试验	根据 GB/T241—2007 标准（P2）规定的试验压力、加压速度和压力传递介质的条件下，稳定一定时间。稳压时间内用目视检查焊管基体的外表面或焊缝，不允许有渗漏爆裂。试验后目视检查焊管整体，不允许产生永久变形
		103	试验后外观检验	保证不允许存在划伤；不允许有扁头，弯管；钢管内外无油污等质量问题
		104	开具报告	严格按照 GB/T241—2007 标准（P2）及内部专用范例进行填报，（一式三份送生产部、质检部、随钢管送酸洗一份）不允许弄虚作假
酸洗检验	减少次品管下道工序	105	标识检验	以测量和称重确认标签与焊管的实际壁厚、规格或混批
		106	不圆度检验	保证钢管的不圆度符合国家标准 GB/T 3091—2015 （P4）
		107	定尺长度检验	保证钢管长度符合国家标准 GB/T 3091—2015（P5）（6 米 , 允许偏差 +20mm）
		108	外径检验	保证钢管的外径符合 GB/T21835—2008 标准（P5）要求范围内
		109	开口检验	检查管端是否有开割现象
		110	裂缝检验	锤震后目测，焊筋处有无开裂现象
		111	接头检验	观看同一只管上是否有对接现象
		112	生锈管检验	目测钢管表面是否有泥土、油漆、油渍和生锈管等
		113	瘪坑检验	目测钢管表面是否有局部因外力造成的坑凹现象
		114	麻面 ( 麻坑 ) 检验	用目测、手触摸钢管表面有无点状的凹凸现象
		115	内焊筋是否合格检验	防止存在无内焊筋（包括假焊）或内焊筋超标等问题；防止焊筋不牢固、不均匀，或低于 0.5mm 为不合格
		116	毛刺检验	目测管端内外是否有不规则的多余部分。处理后，管端毛刺应小于 0.5mm 为合格
		117	吊口检验	防止在挂钩、吊装过程中造成的豁口或变形
		118	筋裂检验	通过弯曲或压扁试验检测钢管的焊筋部位，避免存在细小的裂纹。参考《质量控制与管理制度》P6 第 8 条弯曲试验
		119	刮疤检验	保证焊筋刮疤处平滑，呈圆弧面
		120	免口检验	避免由于原料或机械原因造成的焊缝处折叠重压现象
		121	重皮检验	避免钢管有重皮现象
		122	竹节形	防止钢管表面有竹节凹痕
		123	搭焊检验	目测避免钢管焊筋上有多余对焊现象
		124	结疤检验	目测避免钢管表面有电焊瘤、焊点
		125	砂眼检验	目测避免钢管表面有小孔
		126	割伤检验	观察气割捆扎材料下的管体，保证没有割伤、割坏等情况
		127	有无不利于酸洗镀锌的杂物	目测查看保证无油渍、油漆等不易酸洗杂物，防止漏镀
酸洗钢管	去除钢管表面生成的氧化皮等杂物	128	酸的浓度	用化验方法化验酸浓中的氯化氢含量，控制在 20%—24%
酸洗钢管	去除钢管表面生成的氧化皮等杂物	129	钢管欠酸洗检验	防止①酸洗时间不足、酸液温度低、浓度低（温度应控制在 25—40℃、酸浓度中的氯化氢为 20%—24%）②管捆摇动次数少③炉焊钢管内存在硅酸盐

Control test items	Control detection effect	working procedure	Control and detection link	Control test content
Selected manufacturers	Ensure raw material manufacturer qualification and product quality	1	Evaluation of raw material manufacturers	Quality, credibility and other aspects of comprehensive evaluation, raw material procurement to achieve“quality selection of raw materials”
Selected manufacturers		2	Verify information	Check the information of raw materials provided by the supplier, and enter the yard only after they are correct
Selected raw materials	Raw materials for welded pipe production directly affect the quality of welded pipe	3	Scab examination	Avoid "on the surface of the roll plate; Tongue shape &; Or & lt; Scale &; Of, bonded, irregularly shaped raised metal sheet
		4	Crack inspection	Avoid the gap between the top and bottom of the coiled plate
		5	Layered inspection	Avoid local and obvious metal separation layer on coil section
		6	Bubble inspection	Avoid irregular and round holes with smooth inner wall on the surface or inside of the coil board
		7	Surface slag inclusion inspection	Avoid non-metallic slag inclusion on the surface of rolling plate
		8	Pitting inspection	Avoid small and irregular pits and local rough surface on the surface of rolling plate
		9	Scratch inspection	Avoid straight and fine groove mark on the surface of coil plate
		10	Scratch inspection	Avoid slight straight or curved scratches on the surface of the coil
		11	Indentation inspection	Avoid different shape, size and intermittent dents on the surface of the rolling plate
		12	Roller printing inspection	Avoid the damage of the pressure roller and make the surface of the coil periodically appear convex or concave marks
		13	Rust inspection	Avoid yellow, yellow green, or brown spots on the local surface of the coil
		14	Scale inspection	Avoid too large area of red metal oxide layer formed on the surface of coil plate
		15	Piao Qu inspection	Avoid bending in both longitudinal and transverse directions
		16	Sickle bend inspection	Accord with GB/T 3524—2005 standard（P2）requirement
		17	波浪检查	避免在卷板的全长或局部沿轧制方向的水平面呈起伏不平的且有规律分布的突出（波峰）和凹下（波谷）的弯曲形状
		18	浪皱检查	避免沿轧制方向在卷板的一侧出现起伏不平的海带状弯曲
		19	槽状检查	避免卷板沿横向两侧边同时发生的弧形弯
		20	厚度不均检查	避免卷板纵、横断面厚度不均
		21	毛刺检查	避免在卷板宽度方向的两边出现尖而薄的飞刺
		22	折叠检查	避免使卷板发生的急剧弯曲而形成的折痕或搭迭
		23	宽度检测	防止宽度及其均匀性不符合 GB/T 3524—2005 标准（P4）或采购要求
		24	厚度检测	防止厚度及其均匀性不符合 GB/T 3524—2005 标准（P3）或采购要求，做到“壁厚确保标准”
		25	成分分析	按照 GB/T 4336 标准分析 C、Si、Mn、P、S，结果与来料材质单进行比较，避免材质不符合 GB/T 700 标准要求（P4）
		26	力学试验	按照 GB/T 228 标准对卷板进行横向或纵向拉伸试验，结果与来料材质单进行比较，避免力学性能达不到 GB/T 3524—2005 标准要求（P5）
卷板裁剪	将卷板裁剪成生产不同规格焊管的卷板	27	进料检查	避免卷板表面及边缘有磕碰损坏
		28	剪切检查	检查液压剪子，剪切不齐，切头不得超过有效板面2cm（. 卷板尾部应到机组进行处理
		29	导向辊检查	调整导向辊，防止漏刀
		30	接头检查	避免接头处不平整、焊缝余高不符合 GB/T3091—2015 标准（P8）
		31	圆盘剪检查	检查刀轴和刀套，防止刻刀和原料裁剪的宽窄不均
		32	卷曲检查	进料不能太长，防止卷曲脱落
		33	分料盘检查	防止卷板有漏刀、毛刺、扣边现象
上料转盘	放入卷板，保证卷板打入料笼前准备	34	外观检查	防止卷板表面及边缘有磕碰损坏
卷板切头	将卷板料窄处剪掉，便于焊接	35	剪切要求	将卷板料窄处剪切整齐，与卷板方向垂直，且带头长度部分不得超过有效板面 2cm
卷板对焊	将不同卷的卷板连接在一起送入料笼	36	外观检查	避免接头处不平整、焊缝余高不符合 GB/T3091—2015 标准（P8）
打入料笼	为机组储存一定量的原料，保障机组连续开车生产	37	外观检查	防止表面及边缘有磕碰损坏现象
打入料笼	为机组储存一定量的原料，保障机组连续开车生产	38	打料检查	防止卷板在笼套内卡死或翻料
五辊平整	原料与轧辊同一中心	39	五辊平整	由于卷板在料笼储存时会出现折弯，通过五辊方可较平
钢管成型	将卷板由粗成型转变成精成型（卷成圆管型）	40	成型质量检查	保证焊缝开口角的平整与对称，可根据管径对开口角进行调整。（4 分—1.2 寸开口角为 3—5 度）
挤压成型	保证管坯两边水平性	41	挤压辊检查	防止高低不平，观察挤压辊的挤压力，保持同一高度
高频焊接	将卷成圆筒型的卷板焊接牢固	42	焊接质量检查	避免焊接不牢，脱焊，冷叠
		43		避免焊缝两边出现波纹
		44		避免焊缝有开裂与静裂
		45		避免焊缝不能形成线状
高频焊接	将卷成圆筒型的卷板焊接牢固	46	焊接质量检查	避免出现夹渣
		47		避免出现焊缝外裂纹
		48		避免出现根部收缩
		49		避免出现根部未焊透
		50		避免出现未熔合
		51		避免出现漏焊、假焊、搭焊等现象的出现。（一般卷板在通过加紧辊时，由于高频加热卷板边缘熔化，在焊接时会出现乳白色的晶体颗粒状火花，这说明焊接质量是有保证的）
焊缝刮疤	对外焊缝余高进行削磨处理	52	外观检查	防止转缝、免口及焊口错位现象；要求焊缝无波纹，两侧无焊瘤。
焊缝刮疤	对外焊缝余高进行削磨处理	53	焊缝检查	保证焊缝刮痕、颜色和成型质量情况符合 GB/T13793—2008（P10）要求
循环冷却	对焊管进行冷却	54	水槽水容量检查	根据管径不同，速度快慢，控制水质、水温、水流量、含盐量、酸碱度等
钢管定径	调整焊管外径及不圆度	55	外径检查	控制在 GB/T21835—2008 标准（P5）要求范围内
钢管定径	调整焊管外径及不圆度	56	不圆度检查	控制在 GB/T3091—2015 标准（P4）要求范围内
粗略调直	消除钢管轻微弯曲	57	观察调直设备	使用调直设备，使钢管平直进入下一道工序
无损检测	检测焊缝表面及内部可能影响钢管质量的缺陷	58	检测前仪器调校	设置相关参数；用对比试块确定扫查比例及探伤灵敏度；增加表面补偿，以保证缺陷的检出率
		59	更换规格后首批检验	每次更换产品规格开车后必须进行首批成品检验，检验支数不少于三支，合格后方可生产
		60	焊管基体金属检验	通过目视检查钢管表面的质量缺欠
		61	焊缝外观检验	通过目视检查冷却后的焊缝外观，不允许有焊缝错位、烧伤、结疤、开口、裂缝、筋裂刮疤不平、免口等缺陷存在
		62	金属及焊缝内部质量超声波检测（抽检）	紧贴管体的探头发射超声波，仪器接受并解析反射的回波，根据 SY/T6423.2—1999 调校探测基准灵敏度，通过仪器屏幕上显示的回波波高判断反射体的类型、大小、深度。不允许存在裂纹、回波波高超过满屏 50% 的气孔、未焊透、未融合等严重影响焊缝质量的缺陷。抽检规则：按照每批次 1% 比例进行抽检，如发现问题及时记录和反馈。在缺陷处做好明显的标记，便于工人进行相应的处理；并增加 10% 的抽检率增加抽检过程中仍然存在不合格品，应及时通知机组停车调整生产工艺
飞锯切割	对焊管定尺切割	63	管端检查	管端保证无毛刺、斜口
飞锯切割	对焊管定尺切割	64	定尺长度	根据标准检查测速辊直径，设定合理数据
钢管矫直	调整钢管弯曲度	65	外观检查	避免管体损伤、管口压扁现象；管面不能有压痕
管端齐头	将管口毛刺处理干净	66	管端检查	保证管端光滑无毛刺，保证每根钢管达到“管直头净效果”
成品检验	保证出车间焊管质量符合标准要求	67	外观检查	保证表面钢管表面光滑，不允许有折叠、裂缝、重皮、分层、搭焊等缺陷存在，允许有壁厚负偏差范围的划伤，不允许有严重划伤、焊缝错位、烧伤和结疤
		68	内焊缝检查	保证焊筋牢固，粗细均匀，呈铁丝状，内焊筋应高于 0.5mm，穿线管焊筋不允许有毛刺存在
		69	外径检查	控制在 GB/T21835—2008 标准（P5）要求范围内
		70	不圆度检查	控制在 GB/T3091—2015 标准（P4）要求范围内
		71	定尺长度检测	钢管长度为 6m，根据 GB/T3091—2015 要求直缝高频焊管的总长度允许偏差为 +20mm。（君诚专用管要求：4 分—2 寸 0—5mm、2.5 寸—4 寸 0—10mm、5 寸— 8 寸 0—15mm）
		72	弯曲度检测	根据 GB/T3091—2015 要求钢管全长弯曲度应不大于钢管长度的 0.2%
		73	管端检测	保证管头无毛刺，端头截面符合 GB/T3091—2015 要求
		74	外焊缝检查	外焊缝刮疤应使用圆弧刀，刮疤处应圆弧过渡
		75	豁口检查	避免在管端有开豁现象
		76	裂缝检查	避免在焊筋处有开裂现象
		77	接头检查	避免焊管管体上有对接现象
		78	划伤检查	避免焊管表面有严重划痕，影响壁厚。不能低于壁厚的负偏差（12.5%）
		79	瘪坑检测	防止在焊管局部因外力造成坑凹现象。企业内控标准（4 分—1 寸，瘪坑深度 <2mm；1¼ 寸—2 寸，瘪坑深度 <3mm；2½ 寸—6 寸，瘪坑深度 <4mm；8 寸瘪坑深度 <6mm）
		80	麻面（坑）检查	避免钢管表面有点状的凹痕
		81	内焊筋检查	防止焊筋不牢固、不均匀，低于 0.5mm 为焊筋不合格
		82	毛刺检查	避免管头内外面有不规则的多余部分。企业内控标准（4 分—2 寸毛刺<1mm；2½ 寸— 4 寸毛刺 <2mm；5 寸—8 寸毛刺 <3mm。注：净头管不允许有毛刺）
		83	吊口检查	避免由于挂钩、吊装造成的豁口或变形即“吊口”
		84	筋裂检查	防止在焊筋部位产生细小裂纹
成品检验	保证出车间焊管质量符合标准要求	85	刮疤不平	避免刮疤后焊筋上凹凸不平，焊筋处不是平滑的圆弧面，低于母材的负差视为不平
		86	免口检查	防止由原料或机械原因造成的焊缝处折叠、重压现象，焊筋部位不光滑，有免边、折叠焊缝错位等
		87	重皮检查	避免表面不光滑、有分层、少肉或高低不平现象
		88	结疤检查	避免表面有对母材构成伤害的焊点
		89	砂眼检查	防止钢管表面有孔
		90	斜口检查	防止管的横截面与中心线不垂直，端头应符合 GB/T3091—2015 要求
		91	标识检查	避免管体所粘商标与焊管的实际规格不符或混批
成品包装	依照每件规定数量的钢管进行打包	92	打包带检查	钢管包装为六角形，6 道打包带，均为本厂生产，两端打包带距端 130mm±10mm，中间 4 道要均分，打包带焊接时应对齐、平整，打包带不允许偏斜，打包带对接处应切 45°角，必须符合 GB/T2102—2006（P5）要求
成品包装	依照每件规定数量的钢管进行打包	93	商标检查	内容准确，平面朝上，成品管商标要端正贴在每件管挡板对齐第一道焊接打包带右侧面中间，君诚字迹向内
力学试验	检验材料力学性能	94	弯曲试验	检验 2 寸及以下钢管焊接质量，符合 GB/T3091—2015（P7）要求
		95	压扁试验	检验 2 寸以上钢管焊接质量，符合 GB/T3091—2015（P7）要求
		96	压槽试验	检验钢管压槽性能，符合CECS 151-2003 沟槽式连接管道工程技术规程要求（P9）
		97	拉伸试验	检验钢管抗拉强度及断后伸长率，符合 GB/T3091—2015（P7）要求
水压检验	检查焊管基体金属和焊缝的强度、密闭性及外观质量	98	拆包前检验	避免标签与焊管的实际规格不符或混批不允许拆包（同一炉批号、同一规格一起打压
		99	外观检验	目视检查基体金属 , 防止有裂缝、重皮、严重锈蚀、砂眼等缺陷 , 不允许严重划伤
		100	试验开始前端头检验	通过目视检查焊管两端头表面必须平整光滑。不允许有瘪头、弯管、吊口，端口无毛刺管端头截面与中心线垂直，无斜面，偏差应小于 3°
		101	增压前充填传压介质（水）检验	焊管充填传压介质（水）完毕后，不要急于升压，必须先检查一下系统有无渗液漏液现象
		102	静水压试验	根据 GB/T241—2007 标准（P2）规定的试验压力、加压速度和压力传递介质的条件下，稳定一定时间。稳压时间内用目视检查焊管基体的外表面或焊缝，不允许有渗漏爆裂。试验后目视检查焊管整体，不允许产生永久变形
		103	试验后外观检验	保证不允许存在划伤；不允许有扁头，弯管；钢管内外无油污等质量问题
		104	开具报告	严格按照 GB/T241—2007 标准（P2）及内部专用范例进行填报，（一式三份送生产部、质检部、随钢管送酸洗一份）不允许弄虚作假
酸洗检验	减少次品管下道工序	105	标识检验	以测量和称重确认标签与焊管的实际壁厚、规格或混批
		106	不圆度检验	保证钢管的不圆度符合国家标准 GB/T 3091—2015 （P4）
		107	定尺长度检验	保证钢管长度符合国家标准 GB/T 3091—2015（P5）（6 米 , 允许偏差 +20mm）
		108	外径检验	保证钢管的外径符合 GB/T21835—2008 标准（P5）要求范围内
		109	开口检验	检查管端是否有开割现象
		110	裂缝检验	锤震后目测，焊筋处有无开裂现象
		111	接头检验	观看同一只管上是否有对接现象
		112	生锈管检验	目测钢管表面是否有泥土、油漆、油渍和生锈管等
		113	瘪坑检验	目测钢管表面是否有局部因外力造成的坑凹现象
		114	麻面 ( 麻坑 ) 检验	用目测、手触摸钢管表面有无点状的凹凸现象
		115	内焊筋是否合格检验	防止存在无内焊筋（包括假焊）或内焊筋超标等问题；防止焊筋不牢固、不均匀，或低于 0.5mm 为不合格
		116	毛刺检验	目测管端内外是否有不规则的多余部分。处理后，管端毛刺应小于 0.5mm 为合格
		117	吊口检验	防止在挂钩、吊装过程中造成的豁口或变形
		118	筋裂检验	通过弯曲或压扁试验检测钢管的焊筋部位，避免存在细小的裂纹。参考《质量控制与管理制度》P6 第 8 条弯曲试验
		119	刮疤检验	保证焊筋刮疤处平滑，呈圆弧面
		120	免口检验	避免由于原料或机械原因造成的焊缝处折叠重压现象
		121	重皮检验	避免钢管有重皮现象
		122	竹节形	防止钢管表面有竹节凹痕
		123	搭焊检验	目测避免钢管焊筋上有多余对焊现象
		124	结疤检验	目测避免钢管表面有电焊瘤、焊点
		125	砂眼检验	目测避免钢管表面有小孔
		126	割伤检验	观察气割捆扎材料下的管体，保证没有割伤、割坏等情况
		127	有无不利于酸洗镀锌的杂物	目测查看保证无油渍、油漆等不易酸洗杂物，防止漏镀
酸洗钢管	去除钢管表面生成的氧化皮等杂物	128	酸的浓度	用化验方法化验酸浓中的氯化氢含量，控制在 20%—24%
酸洗钢管	去除钢管表面生成的氧化皮等杂物	129	钢管欠酸洗检验	防止①酸洗时间不足、酸液温度低、浓度低（温度应控制在 25—40℃、酸浓度中的氯化氢为 20%—24%）②管捆摇动次数少③炉焊钢管内存在硅酸盐

home
About
- Group
- Production
- Framework
- Honor
- Development
- Public welfare
Culture
News
- Company news
- Industry News
Products
- Introduce
- Price
- Case
- Encyclopedia
Quality
- Material
- Process
- Testing
- After sales
Contact
- Hotline
- Address
language
- 中文
- English

Contact Us

Service Tel：400-004-7711

Service Tel：010-85763166 85763966
Service Tel：022-28110588 28110688

middle section of Juncheng Road, Caigongzhuang Industrial Park, Jinghai District, Tianjin

Mail：info@jccopipe.com

Telephone : 022-58112636

Fax：022-68568527